G41300 - ASTM A29/A29M-2012

USA UNS	G41300
AISI American Iron and Steel Institute	4130
Corresponding Standard	ASTM A29/A29M-2012 Standard Specification for General Requirements for Steel Bars, Carbon and Alloy, Hot-Wrought
Classification	Alloy Steel

Chemical Element Composition Content (%)

Component	C	Si ^①	Mn	P	S	Cr	Ni ^②	Cu ^②	Mo	More
Minimum Value	0.28	0.15	0.4	-	-	0.8	-	-	0.15	③
Maximum Value	0.33	0.35	0.6	0.035	0.04	1.1	0.25	0.35	0.25	③

① Silicon may be specified by the purchaser as 0.10 % maximum. The need for 0.10% maximum generally relates to severe cold-formed parts.
② residual elements: Ni, Cu
③ Standard alloy steels can be produced with a lead range of 0.15–0.35 %. Such steels are identified by inserting the letter “L” between the second and third numerals of the AISI number, for example, 41 L 40. A cast or heat analysis is not determinable when lead is added to the ladle stream.

Approximate Comparison Table Cold Heading Steel

China		United States		Germany		France	Russia	United Kingdom
GB	ISC	ASTM/AISI	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ML30CrMo	A30304	4130	G41300	≈25CrMo4	1.7218	30CD4	30ХМА	9/0

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!