SUS630-HR - JIS G 4311-2019

Grade	SUS630-HR
Corresponding Standard	JIS G 4311-2019 Heat-Resisting Steel Bars and Wire Rods
Classification	Precipitation-Hardening Stainless Steel
Properties	Corrosion Resistance
Density	7.78 g/cm³

SUS630-HR Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Nb
Minimum Value	-	-	-	-	-	15	3	3	0.15
Maximum Value	0.07	1	1	0.04	0.03	17.5	5	5	0.45

SUS630-HR Mechanical Properties

	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
Bar; d≤75mm	Solution Heat Treatment (S)					≤363
Bar; d≤75mm	Precipitation Hardening (H900)	≥1310	≥1175	≥10	≥40	≥375
Bar; d≤75mm	Precipitation Hardening (H1025)	≥1070	≥1000	≥12	≥45	≥331
Bar; d≤75mm	Precipitation Hardening (H1075)	≥1000	≥860	≥13	≥45	≥302
Bar; d≤75mm	Precipitation Hardening (H1150)	≥930	≥725	≥16	≥50	≥277

SUS630-HR Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!