A515 Grade 65 A515M Grade 450 - ASTM A515/A515M-2017

Grade	A515 Grade 65
Other Names
Corresponding Standard	ASTM A515/A515M-2017 Pressure Vessel Plates, Carbon Steel, for Intermediate- and Higher-Temperature Service
Classification	Carbon Steel

A515 Grade 65 Chemical Element Composition Content (%)

	Component	C ^①	Si	Mn ^①	P	S
t≤25mm	Minimum Value	-	0.15	-	-	-
t≤25mm	Maximum Value	0.28	0.4	0.9	0.025	0.025

	Component	C ^①	Si	Mn ^①	P	S
25mm＜t≤50mm	Minimum Value	-	0.15	-	-	-
25mm＜t≤50mm	Maximum Value	0.31	0.4	0.9	0.025	0.025

	Component	C ^①	Si	Mn ^①	P	S
t＞50mm	Minimum Value	-	0.15	-	-	-
t＞50mm	Maximum Value	0.33	0.4	0.9	0.025	0.025

① For each reduction of 0.01 percentage point below the specified maximum for carbon, an increase of 0.06 percentage point above the specified maximum for manganese is permitted, up to a maximum of 1.50 % by heat analysis and 1.60 % by product analysis.

A515 Grade 65 Mechanical Properties

	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
50mm＜t≤200mm	450~585	≥240	≥19
t≤50mm	450~585	≥240	≥23

Heat treatment:
—Plates 2 in. [50 mm] and under in thickness are normally supplied in the as-rolled condition. The plates may be ordered normalized or stress relieved, or both.
—Plates over 2 in. [50 mm] in thickness shall be normalized.

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!