S42226 - ASTM A565/A565M-2010(R2017)

USA UNS	S42226
Corresponding Standard	ASTM A565/A565M-2010(R2017) Martensitic Stainless Steel Bars for High-Temperature Service
Classification	Martensitic Stainless Steel

Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo	N	W	V	Nb	Al
Minimum Value	0.15	0.2	0.5	-	-	10	0.3	0.8	0.04	-	0.15	0.35	-
Maximum Value	0.2	0.6	0.8	0.02	0.01	11.5	0.6	1.1	0.08	0.25	0.25	0.55	0.05

Mechanical Properties

	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
HT - Heat treated (for high-temperature service)	≥965	≥690	≥15	≥45	≤321	≥11
Annealed					≤302

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!