Grade X6Cr17
Germany W-Nr. 1.4016
Corresponding Standard DIN EN 10263-5-2018
Steel Rod, Bars and Wire for Cold Heading and Cold Extrusion - Part 5: Technical Delivery Conditions for Stainless Steels
Classification Ferritic Stainless Steel
Properties Corrosion Resistance
Density 7.7 g/cm3
X6Cr17 Chemical Element Composition Content (%)
Component C ⓐ Si Mn P S ⓑ Cr
Minimum Value - - - - - 16
Maximum Value 0.08 1 1 0.04 0.03 18
X6Cr17 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
Rod, Wire; 2<d≤5 Softening Annealing + Cold Drawn + Softening Annealing (+A+C+A) ≤560 ≥63
Wire; 2<d≤5 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤620 ≥61
Bar stock, rod stock, wire; 5 < d ≤ 10 Softening Annealing (+A) or Softening Annealing + Pickling (+A+PE) ≤560 ≥63
Wire; 5<d≤10 Softening Annealing + Quenching + Softening Annealing (+A+LC) ≤660 ≥60
Rod, Wire; 5<d≤10 Softening Annealing + Cold Drawn + Softening Annealing (+A+C+A) ≤560 ≥63
Wire; 5<d≤10 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤600 ≥61
Bar stock, rod stock, wire stock; 10 < d ≤ 25 Softening Annealing (+A) or Softening Annealing + Pickling (+A+PE) ≤560 ≥63
Wires; 10<d≤25 Softening Annealing + Quenching + Softening Annealing (+A+LC) ≤640 ≥60
Wires; 10<d≤25 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤560 ≥63
New and Old Grade Replacement List
Corresponding Standard Grade
DIN 1654-5-1989
Grade
Germany W-Nr.
DIN EN 10263-5-2002
Grade
Germany W-Nr.
DIN EN 10263-5-2018
Grade
Germany W-Nr.
1 Approximate Comparison Table Ferritic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
10Cr17
(1Cr17) 		S11710 430 SUS 430 STS 430 430 S43000 X6Cr 17
8
ISO 683-13-1986 		4016-430-00-I X6Cr 17
(X8Cr 17) 		1.4016 Z8C 17 X6Cr 17 1.4016 12Х 17 2320 430S15
2 Approximate Comparison Table Ferritic Stainless Steel
China Japan United States Germany France European Standard Russia Sweden United Kingdom
GB JIS ASTM UNS DIN EN/DIN NF EN/NF EN Numerical Grade GOST SS BS EN/BS
1Cr15 SUS430 430 S43000 X6Cr17 Z8C17 X6Cr17 1.4016 12KH17 2320 430S17
430S18
X6Cr17 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6Cr 17 1.4016
2 ISO 4955-2005
X6Cr17
3 EN 10296-2-2005
X6Cr17 1.4016
4 EN 10263-5-2001
X6Cr17 1.4016
5 EN 10250-4-1999
X6Cr 17 1.4016
6 ISO TS 15510-2003
X6Cr17
7 EN 10088-2-2005
X6Cr 17 1.4016
8 DIN 17440-1972
X6Cr 17 X8Cr 17 1.4016
9 EN 10088-3-2005
X6Cr17 1.4016
10 EN 10297-2-2005
X6Cr17 1.4016
11 ISO 4955-1994
X6Cr17 (H4)
12 EN 10088-3-2014
X6Cr17 1.4016
13 ISO 15510-2014
X6Cr17 4016-430-00-I
14 DIN EN 10263-5-2018
X6Cr17 1.4016
15 DIN EN 10088-3-2014
X6Cr17 1.4016
16 ISO 683-18-2014
X6Cr17 4016-430-00-I
17 ISO 4955-2016
X6Cr17 4016-430-00-I
18 ISO 4954-2018
X6Cr17 4016-430-00-I
19 NF EN 10088-2-2005
X6Cr17 1.4016
20 NF EN 10088-1-2005
X6Cr17 1.4016
21 NF EN 10296-2-2005
X6Cr17 1.4016
22 EN 10263-5-2017
X6Cr17 1.4016
23 DIN EN 10151-2002
X6Cr17 1.4016
24 ISO 4954-2-2024
X6Cr17 4016-430-00-I
25 DIN EN 10296-2-2006
X6Cr17 1.4016
26 DIN 1654-5-1989
X6Cr 17 1.4016
27 DIN EN 10263-5-2002
X6Cr17 1.4016

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!