中文版
Home Material DIN EN 10263-5-2018
简体 | 繁體
Grade X6CrMo17-1
Germany W-Nr. 1.4113
Corresponding Standard DIN EN 10263-5-2018
Steel Rod, Bars and Wire for Cold Heading and Cold Extrusion - Part 5: Technical Delivery Conditions for Stainless Steels
Classification Ferritic Stainless Steel
Properties Corrosion Resistance
Density 7.7 g/cm3
X6CrMo17-1 Chemical Element Composition Content (%)
Component C Si Mn P S ⓑ Cr Mo
Minimum Value - - - - - 16 0.9
Maximum Value 0.08 1 1 0.04 0.03 18 1.4
X6CrMo17-1 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
Rod, Wire; 2<d≤5 Softening Annealing + Cold Drawn + Softening Annealing (+A+C+A) ≤600 ≥60
Wire; 2<d≤5 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤660 ≥58
Bar stock, rod stock, wire; 5 < d ≤ 10 Softening Annealing (+A) or Softening Annealing + Pickling (+A+PE) ≤600 ≥60
Wire; 5<d≤10 Softening Annealing + Quenching + Softening Annealing (+A+LC) ≤710 ≥57
Rod, Wire; 5<d≤10 Softening Annealing + Cold Drawn + Softening Annealing (+A+C+A) ≤600 ≥60
Wire; 5<d≤10 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤640 ≥58
Bar stock, rod stock, wire stock; 10 < d ≤ 25 Softening Annealing (+A) or Softening Annealing + Pickling (+A+PE) ≤600 ≥60
Wires; 10<d≤25 Softening Annealing + Quenching + Softening Annealing (+A+LC) ≤690 ≥57
Wires; 10<d≤25 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤600 ≥60
1 Approximate Comparison Table Ferritic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Sweden United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade SS BS EN/BS
10Cr17Mo
(1Cr17Mo) 		S11790 434 SUS 434 STS 434 434 S43400 X6CrMo 17-1
9c
(ISO 683-13-1986) 		4113-434-00-I X6CrMo 17-1
(X6CrMo 17) 		1.4113
1.4113 		Z8CD 17-01 X6CrMo 17-1 1.4113 2325 434S17
434S19
2 Approximate Comparison Table Plastic Mold Steel
China Japan United States International Organization for Standardization Germany Sweden
GB JIS ASTM ISO DIN EN/DIN W-Nr. SS
3Cr17Mo SUS 434 440 X38CrMo16 X6CrMo 17-1 1.4113 2325
X6CrMo17-1 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6CrMo 17-1 1.4113
2 EN 10263-5-2001
X6CrMo17-1 1.4113
3 ISO TS 15510-2003
X6CrMo17-1
4 EN 10088-3-2005
X6CrMo17-1 1.4113
5 EN 10088-3-2014
X6CrMo17-1 1.4113
6 ISO 15510-2014
X6CrMo17-1 4113-434-00-I
7 DIN EN 10263-5-2018
X6CrMo17-1 1.4113
8 DIN EN 10088-3-2014
X6CrMo17-1 1.4113
9 ISO 683-18-2014
X6CrMo17-1 4113-434-00-I
10 ISO 4954-2018
X6CrMo17-1 4113-434-00-I
11 NF EN 10088-2-2005
X6CrMo17-1 1.4113
12 NF EN 10088-1-2005
X6CrMo17-1 1.4113
13 EN 10263-5-2017
X6CrMo17-1 1.4113
14 ISO 4954-2-2024
X6CrMo17-1 4113-434-00-I

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!