Home Material DIN EN 10263-5-2018
简体 | 繁體
Grade X2CrNi19-11
Germany W-Nr. 1.4306
Corresponding Standard DIN EN 10263-5-2018
Steel rod, bars and wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels
Classification Austenitic Stainless Steel
Properties Corrosion Resistance
X2CrNi19-11 Chemical Element Composition Content (%)
Component C Si Mn P S ⓑ Cr Ni Cu N
Minimum Value - - - - - 18 10 - -
Maximum Value 0.03 1 2 0.045 0.03 20 12 1 0.1
X2CrNi19-11 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
Rod, Wire; 2<d≤5 Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT) ≤680 ≥68
Wire; 2<d≤5 Solid Solution + Cold Drawn + Solid Solution + Quenched Rolling (+AT+C+AT+LC) ≤730 ≥63
Bar, rod, wire; 5<d≤10 Solid Solution (+AT) or Solid Solution + Decap (+AT+PE) ≤630 ≥68
Rod, wire; 5<d≤10 Solid Solution + Cold Drawn (+AT+C) ≤780 -
Rod, Wire; 5<d≤10 Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT) ≤630 ≥68
Wire; 5<d≤10 Solid Solution + Cold Drawn + Solid Solution + Quenched Rolling (+AT+C+AT+LC) ≤680 ≥63
Bar, rod, wire; 10<d≤25 Solid Solution (+AT) or Solid Solution + Decap (+AT+PE) ≤630 ≥68
Rod, wire; 10<d≤25 Solid Solution + Cold Drawn (+AT+C) ≤740 -
Rod, Wire; 10<d≤25 Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT) ≤630 ≥68
Bar, rod, wire; 25<d≤50 Solid Solution (+AT) or Solid Solution + Decap (+AT+PE) ≤630 ≥68
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST BS EN/BS
022Cr19Ni10
(00Cr19Ni10) 		S30403 304L SUS 304L STS 304L 304L S30403 X2CrNi 19-11
X2CrNi 18-9 		4306-304-03-I
4307-304-03-I 		X2CrNi 19-11
(X2CrNi 18-9) 		1.4306 Z2CN 18-10
Z2CN 18-09 		X2CrNi 19-11
X2CrNi 18-9 		1.4306
1.4307 		03Х18Н10 304S12
2 Approximate Comparison Table Corrosion-resistant cast steels
China Japan United States Germany France Russia United Kingdom
GB JIS ASTM DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG00Cr18Ni10 SUS19 CF3 G-X2CrNi18 9 1.4306 Z2CN18.10M Х18Н8Л(旧号) 304C12
X2CrNi19-11 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X2CrNi 19-11 1.4306
2 EN 10296-2-2005
X2CrNi19-11 1.4306
3 EN 10253-4-2003
X2CrNi19-11 1.4306
4 EN 10263-5-2001
X2CrNi19-11 1.4306
5 EN 10250-4-1999
X2CrNi 19-11 1.4306
6 ISO TS 15510-2003
X2CrNi19-11
7 DIN 17440-1972
X2CrNi 19-11 X2CrNi 18-9 1.4306
8 EN 10088-3-2005
X2CrNi 19-11 1.4306
9 EN 10088-3-2014
X2CrNi 19-11 1.4306
10 DIN EN 10263-5-2018
X2CrNi19-11 1.4306
11 ISO 9328-7-2018
X2CrNi19-11
12 DIN EN 10088-3-2014
X2CrNi 19-11 1.4306
13 ISO 683-18-2014
X2CrNi19-11 4306-304-03-I
14 ISO 4954-2018
X2CrNi19-11 4306-304-03-I
15 NF EN 10088-2-2005
X2CrNi19-11 1.4306
16 NF EN 10088-1-2005
X2CrNi19-11 1.4306
17 NF EN 10028-7-2008
X2CrNi19-11 1.4306
18 NF EN 10296-2-2005
X2CrNi19-11 1.4306
19 NF EN 10028-7-2000
X2CrNi19-11 1.4306
20 EN 10263-5-2017
X2CrNi19-11 1.4306
21 ISO 4954-2-2024
X2CrNi19-11 4306-304-03-I
22 DIN EN 10296-2-2006
X2CrNi19-11 1.4306

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!