Home Material DIN EN 10263-5-2018
简体 | 繁體
Grade X6CrNiTi18-10
Germany W-Nr. 1.4541
Corresponding Standard DIN EN 10263-5-2018
Steel rod, bars and wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels
Classification Austenitic Stainless Steel
Properties Corrosion Resistance
Density 7.9 g/cm3
X6CrNiTi18-10 Chemical Element Composition Content (%)
Component C Si Mn P S ⓑ Cr Ni Cu More
Minimum Value - - - - - 17 9 - Ti：5C~0.7
Maximum Value 0.08 1 2 0.045 0.03 19 12 1
X6CrNiTi18-10 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
Rod, Wire; 2<d≤5 Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT) ≤720 ≥65
Wire; 2<d≤5 Solid Solution + Cold Drawn + Solid Solution + Quenched Rolling (+AT+C+AT+LC) ≤770 ≥60
Bar, rod, wire; 5<d≤10 Solid Solution (+AT) or Solid Solution + Decap (+AT+PE) ≤680 ≥65
Rod, wire; 5<d≤10 Solid Solution + Cold Drawn (+AT+C) ≤850 -
Rod, Wire; 5<d≤10 Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT) ≤680 ≥65
Wire; 5<d≤10 Solid Solution + Cold Drawn + Solid Solution + Quenched Rolling (+AT+C+AT+LC) ≤730 ≥60
Bar, rod, wire; 10<d≤25 Solid Solution (+AT) or Solid Solution + Decap (+AT+PE) ≤680 ≥65
Rod, wire; 10<d≤25 Solid Solution + Cold Drawn (+AT+C) ≤810 -
Rod, Wire; 10<d≤25 Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT) ≤680 ≥65
Bar, rod, wire; 25<d≤50 Solid Solution (+AT) or Solid Solution + Decap (+AT+PE) ≤680 ≥65
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr18Ni11Ti S32168 321 SUS 321 STS 321 321 S32100 X6CrNiTi 18-10 4541-321-00-I X6CrNiTi 18-10
(X10CrNiTi 18-9) 		1.4541 Z6CNT 18-10 X6CrNiTi 18-10 1.4541 09Х18Н10Т
Х18Н10Т 		2337 321S12
321S31
2 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr18Ni11Ti
(0Cr18Ni11Ti) 		S32168 321 SUS 321 STS 321 321 S32100 X6CrNiTi 18-10 X6CrNiTi 18-10
(X10CrNiTi 18-9) 		1.4541 Z6CNT 18-10 X6CrNiTi 18-10 1.4541 09Х18Н10Т 2337 321S12
321S31
3 Approximate Comparison Table
China Japan United States Germany France European Standard Russia Sweden United Kingdom
GB JIS ASTM DIN EN/DIN NF EN/NF EN Numerical Grade GOST SS BS EN/BS
0Cr18Ni10Ti
1Cr18Ni11Ti
H0Cr20Ni10Ti 		SUS321 321 X10CrNiTi18-9
X6CrNiTi18-10 		Z6CNT18-10 X6CrNiTi18-10 1.4541 08KH18N10T
08KH18N12T
12KH18N10T 		2337 321S31
X6CrNiTi18-10 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6CrNiTi 18-10 1.4541
2 EN 10296-2-2005
X6CrNiTi18-10 1.4541
3 EN 10253-4-2003
X6CrNiTi18-10 1.4541
4 EN 10263-5-2001
X6CrNiTi18-10 1.4541
5 EN 10250-4-1999
X6CrNiTi 18-10 1.4541
6 ISO TS 15510-2003
X6CrNiTi18-10
7 EN 10088-2-2005
X6CrNiTi18-10 1.4541
8 EN 10088-3-2005
X6CrNiTi 18-10 1.4541
9 ISO 9327(-5)-1999
X6CrNiTi18-10 (F53)
10 EN 10088-3-2014
X6CrNiTi 18-10 1.4541
11 ISO 15510-2014
X6CrNiTi18-10 4541-321-00-I
12 DIN EN 10263-5-2018
X6CrNiTi18-10 1.4541
13 ISO 9328-7-2018
X6CrNiTi18-10
14 DIN EN 10088-3-2014
X6CrNiTi 18-10 1.4541
15 ISO 683-18-2014
X6CrNiTi18-10 4541-321-00-I
16 ISO 4954-2018
X6CrNiTi18-10 4541-321-00-I
17 NF EN 10088-2-2005
X6CrNiTi18-10 1.4541
18 NF EN 10088-1-2005
X6CrNiTi18-10 1.4541
19 NF EN 10028-7-2008
X6CrNiTi18-10 1.4541
20 NF EN 10296-2-2005
X6CrNiTi18-10 1.4541
21 NF EN 10028-7-2000
X6CrNiTi18-10 1.4541
22 EN 10263-5-2017
X6CrNiTi18-10 1.4541
23 ISO 4954-2-2024
X6CrNiTi18-10 4541-321-00-I
24 DIN EN 10296-2-2006
X6CrNiTi18-10 1.4541

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!