X2CrNiMo 17-12-2 1.4404 - DIN EN 10263-5-2018

Grade	X2CrNiMo 17-12-2
Germany W-Nr.	1.4404
Corresponding Standard	DIN EN 10263-5-2018 Steel rod, bars and wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels
Classification	Austenitic Stainless Steel
Properties	Corrosion Resistance

X2CrNiMo 17-12-2 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S ^ⓑ	Cr	Ni	Cu	Mo	N
Minimum Value	-	-	-	-	-	16.5	10	-	2	-
Maximum Value	0.03	1	2	0.045	0.03	18.5	13	1	2.5	0.1

X2CrNiMo 17-12-2 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
Rod, Wire; 2<d≤5	Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT)	≤670	≥68
Wire; 2<d≤5	Solid Solution + Cold Drawn + Solid Solution + Quenched Rolling (+AT+C+AT+LC)	≤720	≥63
Bar, rod, wire; 5<d≤10	Solid Solution (+AT) or Solid Solution + Decap (+AT+PE)	≤650	≥68
Rod, wire; 5<d≤10	Solid Solution + Cold Drawn (+AT+C)	≤780	-
Rod, Wire; 5<d≤10	Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT)	≤650	≥68
Wire; 5<d≤10	Solid Solution + Cold Drawn + Solid Solution + Quenched Rolling (+AT+C+AT+LC)	≤700	≥63
Bar, rod, wire; 10<d≤25	Solid Solution (+AT) or Solid Solution + Decap (+AT+PE)	≤650	≥68
Rod, wire; 10<d≤25	Solid Solution + Cold Drawn (+AT+C)	≤750	-
Rod, Wire; 10<d≤25	Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT)	≤650	≥68
Bar, rod, wire; 25<d≤50	Solid Solution (+AT) or Solid Solution + Decap (+AT+PE)	≤650	≥68

1 Approximate Comparison Table

2 Approximate Comparison Table Heat-resistant cast steels and alloys

X2CrNiMo17-12-2 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!