38B2 1.5515 - EN 10263-4-2017

Grade	38B2
European Standard Steel Grade	1.5515
Corresponding Standard	EN 10263-4-2017 Steel Rod, Bars and Wire For Cold Heading and Cold Extrusion Part 4: Technical Delivery Conditions for Steels for Quenching and Tempering
Classification	Carbon Steel

38B2 Chemical Element Composition Content (%)

Component	C	Si ^ⓔ	Mn	P	S	Cr ^ⓕ	Cu	B
Minimum Value	0.35	-	0.6	-	-	-	-	0.0008
Maximum Value	0.4	0.3	0.9	0.025	0.025	0.3	0.25	0.005

38B2 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
Bar, rod, wire; 5<d≤25	Spheroidizing or Spheroidizing and Peeling (+AC or +AC+PE)	≤570	≥62
Wire; 2<d≤5	Unheated, Cold Drawn, and Spheroidized (+U+C+AC)	≤560	≥64
Wire Rods; 5<d≤25	Unheated, Cold Drawn, and Spheroidized (+U+C+AC)	≤550	≥64
Wire; 2<d≤5	Unheated, Cold Drawn, Spheroidized, and Quenched Rolling (+U+C+AC+LC)	≤600	≥62
Wire Rods; 5<d≤25	Unheated, Cold Drawn, Spheroidized, and Quenched Rolling (+U+C+AC+LC)	≤590	≥62
Wire; 5<d≤10	Spheroidizing + Cold Drawn (+AC+C)	≤660	≥57
Wires; 10<d≤25	Spheroidizing + Cold Drawn (+AC+C)	≤650	≥57

1 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM/AISI	ISO	EN
ML35B GB/T 6478-2015 GB/T 6478-2001	A70354	SWRCHB 234 JIS G3508-1	10B35 ASTM A29/A29M-12 ASTM A510/A510-13	CE35B ISO 4954-1993	38B2 EN 10263-4-2001

2 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

International Organization for Standardization	European Standard
ISO	EN	Numerical Grade
38B2	38B2	1.5515

3 Approximate Comparison Table Cold Heading Steel

China	United States	International Organization for Standardization	European Standard
GB	ASTM	ISO	EN
ML38B	10B38	38B2	38B2

38B2 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!