Grade 5052
Other Names
Corresponding Standard JIS H 4040-2015
Aluminium and Aluminium Alloy Bars and Wires
Classification Aluminum and Aluminum Alloys
Properties Corrosion Resistance Weldability
5052 Chemical Element Composition Content (%)
Component Fe Si Mn Cr Cu Zn Mg Other Individual Other Total More
Minimum Value - - - 0.15 - - 2.2 - - Al:余量
Maximum Value 0.4 0.25 0.1 0.35 0.1 0.1 2.8 0.05 0.15
"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.
5052 Mechanical Properties
condition Mark
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
%
Extruded bar (BE); all sizes 5052 H112 Strain - Only Hardening (H112) ≥175 ≥70 -
Extruded bar (BE); all sizes 5052 O Annealing (O) 175~245 ≥70 A50mm
≥20
Cold drawn bars/wires (BD/W); d≤3 5052 O Annealing (O) 170~220 - -
Cold drawn bars/rods (BD/W); 3<d≤100 5052 O Annealing (O) 170~220 ≥65 A50mm
≥25
Cold drawn bars/wires (BD/W); d≤3 5052 H111 Strain-Hardening (H111) 170~220 - -
Cold drawn bars/rods (BD/W); 3<d≤100 5052 H111 Strain-Hardening (H111) 170~220 ≥65 A50mm
≥25
Cold-drawn bar/Wire (BD/W); 3≤d≤10 5052 H32 Strain-Hardening and Stabilization - 1/4 Hard (H32) 215~255 - -
Cold drawn bars/wires (BD/W); d≤3 5052 H14 Strain-Hardening - 1/2 Hard (H14) ≥235 - -
Cold Drawn Rod/Wire (BD/W); 3<d≤30 5052 H14 Strain-Hardening - 1/2 Hard (H14) ≥235 ≥180 A
≥5
Cold drawn bars/wires (BD/W); d≤3 5052 H34 Strain-Hardening and Stabilization - 1/2 Hard (H34) ≥235 - -
Cold Drawn Rod/Wire (BD/W); 3<d≤30 5052 H34 Strain-Hardening and Stabilization - 1/2 Hard (H34) ≥235 ≥180 A
≥6
Cold drawn bars/rods (BD/W); d ≤ 15 5052 H16 Strain-hardening-3/4 hard (H16) 250~290 ≥200 A50mm
≥3
Cold drawn bars/rods (BD/W); d ≤ 15 5052 H26 Strain - Work hardened and localized annealing - 3/4 hard (H26) 250~290 ≥200 A50mm
≥3
Cold drawn bars/rods (BD/W); d ≤ 15 5052 H36 Strain-hardening and stabilization - 3/4 hard (H36) 250~290 ≥200 A50mm
≥3
Cold drawn bars/wires (BD/W); d≤10 5052 H18 Strain - Hardening - 4/4 Hard (H18) ≥270 ≥220 A
≥2
Cold drawn bars/wires (BD/W); d≤10 5052 H38 Strain-Hardening and Stabilization - 4/4 Hard (H38) ≥270 ≥220 A
≥2
① A50mm、A（5.65√S0）- gauge length，S0-Specimen area，s=S0，unit mm sq
② d-diameter、thickness or width across flats, unit mm；s - cross section area, unit mm sq
Approximate Comparison Table Aluminium and Aluminium Alloy
Japan United States International Organization for Standardization Germany France European Standard Sweden United Kingdom
JIS UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade SS BS EN/BS
5052 A95052 AlMg2 AlMg1.8
AlMg2.5 		3.3326 5052 ENAW-AlMg2(B) ENAW-5051A AlMg2.5 5251
5052 Corresponding Standards(Same grade name, different standards)
1 GB /T 3190-2008
5052
2 JIS H 4040-2006
5052 A5052 BD A5052 BE A5052 W
3 GB /T 3195-2016
5052
4 DIN 1725-1-1983
5052 AlMg2.5 3.3523
5 GB /T 3190-2020
5052
6 JIS H 4040-2015
5052 A5052 BD A5052 BE A5052 W
7 GB /T 3191-2019
5052
8 GB /T 3880.1-2012
5052