简体 | 繁體
USA UNS S31603
AISI
American Iron and Steel Institute		 316L
Other Names
Corresponding Standard ASTM A959-2019
Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Classification Austenitic Stainless Steel
Properties Strength Corrosion Resistance Low-Temperature Toughness Forgability Weldability
Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni Mo
Minimum Value - - - - - 16 10 2
Maximum Value 0.03 1 2 0.045 0.03 18 14 3
• Unless otherwise indicated, a grade designation originally assigned by the American Iron and Steel Institute (AISI).
1 Approximate Comparison Table Austenitic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
022Cr17Ni12Mo2
(00Cr17Ni14Mo2) 		S31603 316L SUS 316L STS 316L 316L S31603 X2CrNiMo 17-12-2
X2CrNiMo17-12-3 		4404-316-03-I
4432-316-03-I 		X2CrNiMo 18-14-3
(X2CrNiMo 18-12) 		1.4435 Z2CND 17-13 X2CrNiMo 17-12-2
X2CrNiMo17-12-3 		1.4404
1.4432 		03Х17Н14М2 2353 316S11
316S12
2 Approximate Comparison Table Stainless Steels for Cold Heading and Cold Extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
022Cr17Ni12Mo2
(00Cr17Ni14Mo2) 		S31603 SUS316L 316L S31603 X2CrNiMo17-12-2 4404-316-03-I X2CrNiMo17-12-2 1.4404
3 Approximate Comparison Table Stainless Steels for Cold Heading and Cold Extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
022Cr17Ni12Mo2
(00Cr17Ni14Mo2) 		S31603 SUS316L 316L S31603 X2CrNiMo17-12-3 4432-316-03-I X2CrNiMo17-12-3 1.4432

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!