C60 1.0601 - DIN 17200-1987

Grade	C60
Germany W-Nr.	1.0601
Corresponding Standard	DIN 17200-1987 Steels for Quenching and Tempering; Technical Delivery Conditions
Classification	Carbon Steel

C60 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Pb ^*
Minimum Value	0.57	-	0.6	-	-	0.15
Maximum Value	0.65	0.4	0.9	0.045	0.045	0.33

C60 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
Steel; All Sizes	Shearable condition (C)					≤255
Steel; All Sizes	Softening Annealing (G)					≤241
Steel; d≤16	Quenching and Tempering (V)	850~1000	≥580	≥11	≥20
Steel; 16<d≤40	Quenching and Tempering (V)	800~950	≥520	≥13	≥25
Steel; 40<d≤100	Quenching and Tempering (V)	750~900	≥450	≥14	≥30
Bars; 16<d≤100	Normalizing (N)	690~880	≥380		≥14
Flat steel; d≤16	Normalizing (N)	650~920	≥380		Longitudinal ≥14
Flat steel; 16<d≤100	Normalizing (N)	650~920	≥340		≥14
Flat Steel; 100<d≤160	Normalizing (N)	630~880	≥310		≥12

New and Old Grade Replacement List

1 Approximate Comparison Table High-Quality Carbon Structural Steel

China	Japan	United States	International Organization for Standardization	Germany	European Standard		Russia	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	EN	Numerical Grade	GOST	BS EN/BS
60	S58C	1060	C60	C60	C60	1.0601	60 60G	070M60

2 Approximate Comparison Table High-Quality Carbon Structural Steel

China	Japan	United States	International Organization for Standardization	Germany		France	Russia	United Kingdom
GB	JIS	ASTM/AISI	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
60Mn	SWRH62B	1060 1061	Type SC Type DC	C60	1.0601	C60	60г	C60 080A57 080A62

C60 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!