25CrMoS4 1.7213 - DIN 17200-1987

Grade	25CrMoS4
Germany W-Nr.	1.7213
Corresponding Standard	DIN 17200-1987 Steels for Quenching and Tempering; Technical Delivery Conditions
Classification	Alloy Steel

25CrMoS4 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Mo
Minimum Value	0.22	-	0.6	-	0.02	0.9	0.15
Maximum Value	0.29	0.4	0.9	0.035	0.035	1.2	0.3

25CrMoS4 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
Steel; All Sizes	Shearable condition (C)					≤255
Steel; All Sizes	Softening Annealing (G)					≤212
Steel; d≤16	Quenching and Tempering (V)	900~1100	≥700	≥12	≥50		ISO-V ≥45
Steel; 16<d≤40	Quenching and Tempering (V)	800~950	≥600	≥14	≥55		≥50
Steel; 40<d≤100	Quenching and Tempering (V)	700~850	≥450	≥15	≥60		≥50
Steel; 100<d≤160	Quenching and Tempering (V)	650~800	≥400	≥16	≥60		≥45

Approximate Comparison Table Alloy Steel for Quenching and Tempering

International Organization for Standardization	Germany		France	European Standard
ISO	DIN EN/DIN	W-Nr.	NF EN/NF	EN	Numerical Grade
25CrMoS4	25CrMoS4	1.7213	25CD4u	25CrMoS4	1.7213

25CrMoS4 Corresponding Standards(Same grade name, different standards)