36CrNiMo4 1.6511 - DIN 17200-1987

Grade	36CrNiMo4
Germany W-Nr.	1.6511
Corresponding Standard	DIN 17200-1987 Steels for Quenching and Tempering; Technical Delivery Conditions
Classification	Alloy Steel

36CrNiMo4 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo
Minimum Value	0.32	-	0.5	-	-	0.9	0.9	0.15
Maximum Value	0.4	0.4	0.8	0.035	0.03	1.2	1.2	0.3

36CrNiMo4 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
Steel; All Sizes	Softening Annealing (G)					≤248
Steel; d≤16	Quenching and Tempering (V)	1100~1300	≥900	≥10	≥45		ISO-V ≥35
Steel; 16<d≤40	Quenching and Tempering (V)	1000~1200	≥800	≥11	≥50		≥40
Steel; 40<d≤100	Quenching and Tempering (V)	900~1100	≥700	≥12	≥55		≥45
Steel; 100<d≤160	Quenching and Tempering (V)	800~950	≥600	≥13	≥60		≥45
Steel; 160<d≤250	Quenching and Tempering (V)	750~900	≥550	≥14	≥60		≥45

1 Approximate Comparison Table Structural Alloy Steel

2 Approximate Comparison Table Structural Alloy Steel

Japan	United States	International Organization for Standardization	Germany	France	European Standard		Russia	United Kingdom
JIS	ASTM	ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	GOST	BS EN/BS
SCNM439	Gr.9840	36CrNiMo4	36CrNiMo4	40NCD3	36CrNiMo4	1.6511	40KHN2MA	817A37 817M37

36CrNiMo4 Corresponding Standards(Same grade name, different standards)

1	ISO 683-18-1996
	36CrNiMo4
2	DIN 17200-1987
	36CrNiMo4 1.6511
3	ISO 683-1-1987
	36CrNiMo4 36CrNiMo4H 36CrNiMo4HH 36CrNiMo4HL
4	EN 10250-3-1999
	36CrNiMo4 1.6511
5	EN 10297-1-2003
	36CrNiMo4 1.6511
6	DIN 17204-1990
	36CrNiMo4 1.6511
7	ISO 683-2-2016
	36CrNiMo4
8	ISO 683-18-2014
	36CrNiMo4
9	EN ISO 683-2-2018
	36CrNiMo4

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!