C35E - DIN EN ISO 683-1-2018

Grade	C35E
Corresponding Standard	DIN EN ISO 683-1-2018 Heat-Treatable Steels,alloy Steels and Free-Cutting Steels--Part 1: Non-Alloy Steels for Quenching and Tempering
Classification	Carbon Steel

C35E Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	More
Minimum Value	0.32	0.1	0.5	-	-	-	-	-	-	Cr+Mo+Ni≤0.63
Maximum Value	0.39	0.4	0.8	0.025	0.035	0.4	0.4	0.3	0.1	Cr+Mo+Ni≤0.63

C35E Mechanical Properties

	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
d≤16; t≤8	Quenching and Tempering	630~780	≥430	≥17	≥40		≥25
16＜d≤40；8＜t≤20	Quenching and Tempering	600~750	≥380	≥19	≥45		≥25
40＜d≤100；20＜t≤60	Quenching and Tempering	550~700	≥320	≥20	≥50		≥25
d≤16；t≤16	Normalizing (N)	≥550	≥300	≥18
16<d≤100；16＜t≤100	Normalizing (N)	≥520	≥270	≥19
100<d≤250；100＜t≤250	Normalizing (N)	≥500	≥245	≥19
d≤100；t≤100	Flame or Induction Quenching					HRC ≥48

New and Old Grade Replacement List

Approximate Comparison Table High-Quality Carbon Structural Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

U20352

S35C

SM35C

1035

G10350

C35E4

C35E
Ck35

1.1181

C35E
XC38

1572

C35E
080M36

C35E Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!