C60E - DIN EN ISO 683-1-2018

Grade	C60E
Corresponding Standard	DIN EN ISO 683-1-2018 Heat-treatable steels,alloy steels and free-cutting steels--Part 1: Non-alloy steels for quenching and tempering
Classification	Carbon Steel

C60E Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	More
Minimum Value	0.57	0.1	0.6	-	-	-	-	-	-	Cr+Mo+Ni≤0.63
Maximum Value	0.65	0.4	0.9	0.025	0.035	0.4	0.4	0.3	0.1	Cr+Mo+Ni≤0.63

C60E Mechanical Properties

	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
d≤16; t≤8	Quenching and Tempering	850~1000	≥580	≥11	≥25
16＜d≤40；8＜t≤20	Quenching and Tempering	800~950	≥520	≥13	≥30
40＜d≤100；20＜t≤60	Quenching and Tempering	750~900	≥450	≥14	≥35
d≤16；t≤16	Normalizing (N)	≥710	≥380	≥10
16<d≤100；16＜t≤100	Normalizing (N)	≥670	≥340	≥11
100<d≤250；100＜t≤250	Normalizing (N)	≥650	≥310	≥11
All Sizes	Shearable Condition (+S)					≤255
All Sizes	Softening Annealing (+A)					≤241

New and Old Grade Replacement List

Approximate Comparison Table High-Quality Carbon Structural Steel

China		United States		International Organization for Standardization	Germany		France	Russia	Sweden	United Kingdom
GB	ISC	ASTM/AISI	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS	BS EN/BS
60	U20602	1060	G10600	C60E4	C60E Ck60	1.1221	C60E XC60	60	1678	C60E 070M60

C60E Corresponding Standards(Same grade name, different standards)