Grade X2CrNiMoN 17-13-3
Germany W-Nr. 1.4429
Corresponding Standard DIN EN 10088-3-2014
Stainless steels – Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
Classification Austenitic Stainless Steel
X2CrNiMoN 17-13-3 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni ⓓ Mo N
Minimum Value - - - - - 16.5 11 2.5 0.12
Maximum Value 0.03 1 2 0.045 0.015 18.5 14 3 0.22
① Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.
X2CrNiMoN 17-13-3 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW 		Impact Energy Absorption
KV2
J
Bar, rod, wire, section, bright products; d≤160 +AT 580~800 ≥280 (long.)
≥40		 ≤250 (long.)
≥100
Bar, rod, wire, section, bright products; 160<d≤250 +AT 580~800 ≥280 (tr.)
≥30		 ≤250 (tr.)
≥60
+AT=solution annealed；+A=annealed；+QT = quenched and tempered；+P=precipitation hardening；+C=Cold worked，+Csuffix followed by a number represents the tensile strength grade, i.e., the minimum tensile strength value.
long.=longitudinal；tr.=transverse
d=diameter or thickness；Unit mm
New and Old Grade Replacement List
Corresponding Standard Grade
DIN 17440-1972
Grade
Germany W-Nr.
Other Name
DIN EN 10088-3-2014
Grade
Germany W-Nr.
Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade SS BS EN/BS
022Cr17Ni12Mo2N
(00Cr17Ni13Mo2N) 		S31653 316LN SUS 316LN STS 316LN 316LN S31653 X2CrNiMoN 17-12-2
X2CrNiMoN 17-11-2 		X2CrNiMoN 17-13-3
(X2CrNiMoN 18-13) 		1.4429 Z2CND 17-13Az
Z3CND 17-12Az 		X2CrNiMoN 17-13-3
X2CrNiMoN 17-12-2 		1.4429
1.4406 		2375 316S63
316S61
X2CrNiMoN17-13-3 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X2CrNiMoN 17-13-3 1.4429
2 EN 10296-2-2005
X2CrNiMoN17-13-3 1.4429
3 EN 10253-4-2003
X2CrNiMoN 17-13-3 1.4429
4 EN 10263-5-2001
X2CrNiMoN17-13-3 1.4429
5 EN 10269-2006
X2CrNiMoN17-13-3 1.4429
6 EN 10250-4-1999
X2CrNiMoN 17-13-3 1.4429
7 EN 10088-2-2005
X2CrNiMoN 17-13-3 1.4429
8 DIN 17440-1972
X2CrNiMoN 17-13-3 X2CrNiMoN 18-13 1.4429
9 EN 10088-3-2005
X2CrNiMoN 17-13-3 1.4429
10 EN 10297(2)-2005
X2CrNiMoN 17-13-3 1.4429
11 EN 10269-2013
X2CrNiMoN 17-13-3 1.4429
12 EN 10088-3-2014
X2CrNiMoN 17-13-3 1.4429
13 NF EN 10269-1999
X2CrNiMoN17-13-3 1.4429
14 DIN EN 10263-5-2018
X2CrNiMoN 17-13-3 1.4429
15 DIN EN 10269-2014
X2CrNiMoN 17-13-3 1.4429
16 ISO 9328-7-2018
X2CrNiMoN17-13-3
17 DIN EN 10088-3-2014
X2CrNiMoN 17-13-3 1.4429
18 ISO 4954-2018
X2CrNiMoN17-13-3 4429-316-53-I
19 NF EN 10088-2-2005
X2CrNiMoN17-13-3 1.4429
20 NF EN 10088-1-2005
X2CrNiMoN17-13-3 1.4429
21 NF EN 10028-7-2008
X2CrNiMoN17-13-3 1.4429
22 NF EN 10296-2-2005
X2CrNiMoN17-13-3 1.4429
23 NF EN 10028-7-2000
X2CrNiMoN17-13-3 1.4429
24 EN 10263-5-2017
X2CrNiMoN 17-13-3 1.4429
25 ISO 4954-2-2024
X2CrNiMoN17-13-3 4429-316-53-I
26 DIN EN 10296-2-2006
X2CrNiMoN17-13-3 1.4429

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!