X1CrNiMoCuNW 24-22-6 1.4659 - DIN EN 10088-3-2014

Grade	X1CrNiMoCuNW 24-22-6
Germany W-Nr.	1.4659
Corresponding Standard	DIN EN 10088-3-2014 Stainless Steels – Part 3: Technical Delivery Conditions for Semi-Finished Products, Bars, Rods, Wire, Sections and Bright Products of Corrosion Resisting Steels for General Purposes
Classification	Austenitic Stainless Steel
Properties	Corrosion Resistance
Density	8.2 g/cm³

X1CrNiMoCuNW 24-22-6 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu ^ⓒ	Mo	N	W
Minimum Value	-	-	2	-	-	23	21	1	5.5	0.35	1.5
Maximum Value	0.02	0.7	4	0.03	0.01	25	23	2	6.5	0.5	2.5

① Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X1CrNiMoCuNW 24-22-6 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW	Impact Energy Absorption KV2 J
Bar, rod, wire, section, bright products; d≤160	+AT	800~1000	≥420	(long.) ≥50	≤290	(long.) ≥90

+AT=solution annealed；+A=annealed；+QT = quenched and tempered；+P=precipitation hardening；+C=Cold worked，+Csuffix followed by a number represents the tensile strength grade, i.e., the minimum tensile strength value.
long.=longitudinal；tr.=transverse
d=diameter or thickness；Unit mm

X1CrNiMoCuNW24-22-6 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X1CrNiMoCuNW 24-22-6 1.4659
2	ISO TS 15510-2003
	X1CrNiMoCuNW24-22-6
3	EN 10088-2-2005
	X1CrNiMoCuNW 24-22-6 1.4659
4	EN 10088-3-2014
	X1CrNiMoCuNW 24-22-6 1.4659
5	ISO 15510-2014
	X1CrNiMoCuNW24-22-6 4659-312-66-I
6	DIN EN 10088-3-2014
	X1CrNiMoCuNW 24-22-6 1.4659
7	NF EN 10088-2-2005
	X1CrNiMoCuNW24-22-6 1.4659
8	NF EN 10088-1-2005
	X1CrNiMoCuNW24-22-6 1.4659

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!