Home Material DIN EN 10088-3-2014
简体 | 繁體
Grade X6Cr17
Germany W-Nr. 1.4016
Corresponding Standard DIN EN 10088-3-2014
Stainless Steels – Part 3: Technical Delivery Conditions for Semi-Finished Products, Bars, Rods, Wire, Sections and Bright Products of Corrosion Resisting Steels for General Purposes
Classification Ferritic Stainless Steel
Properties Corrosion Resistance
X6Cr17 Chemical Element Composition Content (%)
Component C Si Mn P S ⓑ Cr
Minimum Value - - - - - 16
Maximum Value 0.08 1 1 0.04 0.03 18
① Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.
X6Cr17 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
Bars, rods, wires, profiles, bright products; d≤100 +A 400~630 ≥240 ≥20 ≤200
Cold drawn, precision bar; d≤10 +A 500~750 ≥320 ≥8
Cold drawn, precision bar; 10<d≤16 +A 480~750 ≥300 ≥8
Cold drawn, precision bar; 16<d≤40 +A 400~700 ≥240 ≥15
Cold drawn, precision bar; 40<d≤63 +A 400~700 ≥240 ≥15
Cold drawn, precision processed bar stock; 63 < d ≤ 100 +A 400~630 ≥240 ≥20
Cold drawn wire; d≥0.05 +C500 500~700
Cold drawn wire; d≥0.05 +C600 600~800
Cold drawn wire; d≥0.05 +C700 700~900
Cold drawn wire; d≥0.05 +C800 800~1000
Cold drawn wire; d≥0.05 +C900 900~1100
Cold drawn wire; 0.05<d≤0.1 +A ≤950 ≥10
Cold drawn wire; 0.1<d≤0.2 +A ≤900 ≥10
Cold drawn wire; 0.2<d≤0.5 +A ≤850 ≥15
Cold drawn wire; 0.5<d≤1 +A ≤850 ≥15
Cold drawn wire; 1<d≤3 +A ≤800 ≥15
Cold drawn wire; 3<d≤5 +A ≤750 ≥15
Cold-drawn wire; 5<d≤16 +A ≤700 ≥20
+AT=solution annealed；+A=annealed；+QT = quenched and tempered；+P=precipitation hardening；+C=Cold worked，+Csuffix followed by a number represents the tensile strength grade, i.e., the minimum tensile strength value.
long.=longitudinal；tr.=transverse
d=diameter or thickness；Unit mm
New and Old Grade Replacement List
Corresponding Standard Grade
DIN 17440-1972
Grade
Germany W-Nr.
Other Name
DIN EN 10088-3-2014
Grade
Germany W-Nr.
1 Approximate Comparison Table Ferritic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
10Cr17
(1Cr17) 		S11710 430 SUS 430 STS 430 430 S43000 X6Cr 17
8
ISO 683-13-1986 		4016-430-00-I X6Cr 17
(X8Cr 17) 		1.4016 Z8C 17 X6Cr 17 1.4016 12Х 17 2320 430S15
2 Approximate Comparison Table Ferritic Stainless Steel
China Japan United States Germany France European Standard Russia Sweden United Kingdom
GB JIS ASTM UNS DIN EN/DIN NF EN/NF EN Numerical Grade GOST SS BS EN/BS
1Cr15 SUS430 430 S43000 X6Cr17 Z8C17 X6Cr17 1.4016 12KH17 2320 430S17
430S18
X6Cr17 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6Cr 17 1.4016
2 ISO 4955-2005
X6Cr17 (4)
3 EN 10296-2-2005
X6Cr17 1.4016
4 EN 10263-5-2001
X6Cr17 1.4016
5 EN 10250-4-1999
X6Cr 17 1.4016
6 ISO TS 15510-2003
X6Cr17
7 EN 10088-2-2005
X6Cr 17 1.4016
8 DIN 17440-1972
X6Cr 17 X8Cr 17 1.4016
9 EN 10088-3-2005
X6Cr17 1.4016
10 EN 10088-3-2014
X6Cr17 1.4016
11 ISO 15510-2014
X6Cr17 4016-430-00-I
12 DIN EN 10263-5-2018
X6Cr17 1.4016
13 DIN EN 10088-3-2014
X6Cr17 1.4016
14 ISO 683-18-2014
X6Cr17 4016-430-00-I
15 ISO 4955-2016
X6Cr17 4016-430-00-I (4)
16 ISO 4954-2018
X6Cr17 4016-430-00-I
17 NF EN 10088-2-2005
X6Cr17 1.4016
18 NF EN 10088-1-2005
X6Cr17 1.4016
19 NF EN 10296-2-2005
X6Cr17 1.4016
20 EN 10263-5-2017
X6Cr17 1.4016
21 DIN EN 10151-2002
X6Cr17 1.4016
22 ISO 4954-2-2024
X6Cr17 4016-430-00-I
23 DIN EN 10296-2-2006
X6Cr17 1.4016

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!