X2CrMoTiS 18-2 1.4523 - DIN EN 10088-3-2014

Grade	X2CrMoTiS 18-2
Germany W-Nr.	1.4523
Corresponding Standard	DIN EN 10088-3-2014 Stainless steels – Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
Classification	Ferritic Stainless Steel
Properties	Corrosion Resistance
Density	7.7 g/cm³

X2CrMoTiS 18-2 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Mo	More
Minimum Value	-	-	-	-	0.15	17.5	2	(C+N)≤0.040；Ti:[4x(C+N) + 0.15] ~0.8*
Maximum Value	0.03	1	0.5	0.04	0.35	19	2.5	(C+N)≤0.040；Ti:[4x(C+N) + 0.15] ~0.8*

① Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X2CrMoTiS 18-2 Mechanical Properties

condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Bars, rods, wires, profiles, bright products; d≤100	430~600	≥280	≥15	≤200

+AT=solution annealed；+A=annealed；+QT = quenched and tempered；+P=precipitation hardening；+C=Cold worked，+Csuffix followed by a number represents the tensile strength grade, i.e., the minimum tensile strength value.
long.=longitudinal；tr.=transverse
d=diameter or thickness；Unit mm

X2CrMoTiS18-2 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X2CrMoTiS 18-2 1.4523
2	ISO TS 15510-2003
	X2CrMoTiS18-2
3	EN 10088-3-2014
	X2CrMoTiS 18-2 1.4523
4	ISO 15510-2014
	X2CrMoTiS18-2 4523-182-35-I
5	DIN EN 10088-3-2014
	X2CrMoTiS 18-2 1.4523
6	NF EN 10088-1-2005
	X2CrMoTiS18-2 1.4523

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!