X15Cr 13 1.4024 - DIN EN 10088-3-2014

Grade	X15Cr 13
Germany W-Nr.	1.4024
Corresponding Standard	DIN EN 10088-3-2014 Stainless steels – Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
Classification	Martensitic Stainless Steel
Properties	Corrosion Resistance

X15Cr 13 Chemical Element Composition Content (%)

Component	C ^ⓒ	Si	Mn	P	S ^ⓑ	Cr
Minimum Value	0.12	-	-	-	-	12
Maximum Value	0.17	1	1	0.04	0.03	14

① Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X15Cr 13 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Bar, rod, wire, section, bright products	+A	≤730			≤220
Bar, rod, wire, section, bright products; d≤160	+QT650	650~850	≥450	(long.) ≥15

+AT=solution annealed；+A=annealed；+QT = quenched and tempered；+P=precipitation hardening；+C=Cold worked，+Csuffix followed by a number represents the tensile strength grade, i.e., the minimum tensile strength value.
long.=longitudinal；tr.=transverse
d=diameter or thickness；Unit mm

1 Approximate Comparison Table

China		Taiwan, China	Japan	South Korea	Germany		European Standard		United Kingdom
GB	ISC	CNS	JIS	KS	DIN EN/DIN	W-Nr.	EN	Numerical Grade	BS EN/BS
13Cr13Mo (1Cr13Mo)	S45710	410J1	SUS 410J1	STS 410J1	X15Cr 13	1.4024	X15Cr 13	1.4024	420S29

2 Approximate Comparison Table

China		Taiwan, China	Japan	South Korea	International Organization for Standardization	Germany		United Kingdom
GB	ISC	CNS	JIS	KS	ISO	DIN EN/DIN	W-Nr.	BS EN/BS
13Cr13Mo (1Cr13Mo)	S45710	410J1	SUS 410J1	STS 410J1	X12CrMo 12-6	X15Cr 13	1.4024	420S29

3 Approximate Comparison Table Corrosion-resistant cast steels

China	Japan	United States	Germany		France	Russia	United Kingdom
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG1Cr13	SUS1	CA15	G-X8Cr14 X15Cr13	1.4008 1.4024	Z12C13M	15Х13Л	410C21

X15Cr13 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X15Cr 13 1.4024
2	DIN 17440-1972
	X15Cr 13 1.4024
3	EN 10088-3-2005
	X15Cr 13 1.4024
4	EN 10088-3-2014
	X15Cr 13 1.4024
5	ISO 15510-2014
	X15Cr13 4024-410-09-E
6	DIN EN 10088-3-2014
	X15Cr 13 1.4024
7	DIN 17442-1977
	X15Cr13 1.4024
8	NF EN 10088-2-2005
	X15Cr13 1.4024
9	NF EN 10088-1-2005
	X15Cr13 1.4024

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!