X50CrMoV15 1.4116 - DIN EN 10088-3-2014

Grade	X50CrMoV15
Germany W-Nr.	1.4116
Corresponding Standard	DIN EN 10088-3-2014 Stainless steels – Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
Classification	Martensitic Stainless Steel
Properties	Corrosion Resistance

X50CrMoV15 Chemical Element Composition Content (%)

Component	C ^ⓒ	Si	Mn	P	S ^ⓑ	Cr	Mo	N ^ⓓ	V
Minimum Value	0.45	-	-	-	-	14	0.5	-	0.1
Maximum Value	0.55	1	1	0.04	0.03	15	0.8	0.15	0.2

① Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X50CrMoV15 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
Bar, rod, wire, section, bright products	+A	≤900	≤280

+AT=solution annealed；+A=annealed；+QT = quenched and tempered；+P=precipitation hardening；+C=Cold worked，+Csuffix followed by a number represents the tensile strength grade, i.e., the minimum tensile strength value.
long.=longitudinal；tr.=transverse
d=diameter or thickness；Unit mm

X50CrMoV15 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X50CrMoV 15 1.4116
2	EN 10088-3-2005
	X50CrMoV15 1.4116
3	EN 10088-3-2014
	X50CrMoV15 1.4116
4	ISO 15510-2014
	X50CrMoV15 4116-420-77-E
5	DIN EN 10088-3-2014
	X50CrMoV15 1.4116
6	NF EN 10088-2-2005
	X50CrMoV15 1.4116
7	NF EN 10088-1-2005
	X50CrMoV15 1.4116

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!