X46CrS13 1.4035 - DIN EN 10088-3-2014

Grade	X46CrS13
Germany W-Nr.	1.4035
Corresponding Standard	DIN EN 10088-3-2014 Stainless steels – Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
Classification	Martensitic Stainless Steel
Properties	Corrosion Resistance

X46CrS13 Chemical Element Composition Content (%)

Component	C ^ⓓ	Si	Mn	P	S	Cr
Minimum Value	0.43	-	-	-	0.15	12
Maximum Value	0.5	1	2	0.04	0.35	14

① Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X46CrS13 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Hardness HBW
Bar, Rod, Wire, Profile, Bright Products; d≤63	+A	≤800	≤245
Cold drawn, precision bar; d≤10	+A	≤880	≤280
Cold drawn, precision bar; 10<d≤16	+A	≤880	≤280
Cold drawn, precision bar; 16<d≤40	+A	≤800	≤250
Cold drawn, precision bar; 40<d≤63	+A	≤760	≤230

+AT=solution annealed；+A=annealed；+QT = quenched and tempered；+P=precipitation hardening；+C=Cold worked，+Csuffix followed by a number represents the tensile strength grade, i.e., the minimum tensile strength value.
long.=longitudinal；tr.=transverse
d=diameter or thickness；Unit mm

X46CrS13 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X46CrS 13 1.4035
2	EN 10088-3-2005
	X46CrS13 1.4035
3	EN 10088-3-2014
	X46CrS13 1.4035
4	ISO 15510-2014
	X46CrS13 4035-420-74-E
5	DIN EN 10088-3-2014
	X46CrS13 1.4035
6	NF EN 10088-1-2005
	X46CrS13 1.4035

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!