9SMn 36 1.0736 - DIN 1651-1988

Grade	9SMn 36
Germany W-Nr.	1.0736
Corresponding Standard	DIN 1651-1988 Free-Cutting Steels Technical Delivery Conditions
Classification	Alloy Steel
Properties	Machinability

9SMn 36 Chemical Element Composition Content (%)

Component	C	Si	Mn	P ^*	S
Minimum Value	-	-	1.1	-	0.34
Maximum Value	0.15	0.05	1.5	0.1	0.4

①Elements not listed in the table (except for finishing the cast) shall not be intentionally add to the steel. Such introduction may only be agreed upon with the customer if it can be demonstrated to improve machinability.

9SMn 36 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Bars, semi-finished products, wire; t＜10	Hot Working (U) or Hot Working + Descaling (U+SH)	390~590			≤174
Bars, semi-finished products, wire; 10≤t<16	Hot Working (U) or Hot Working + Descaling (U+SH)	390~590			≤174
Bars, semi-finished products, wire; 16≤t<40	Hot Working (U) or Hot Working + Descaling (U+SH)	380~550			≤163
Bars, semi-finished products, wire; 40≤t<63	Hot Working (U) or Hot Working + Descaling (U+SH)	370~540			≤159
Bars, semi-finished products, wire; 63≤t＜100	Hot Working (U) or Hot Working + Descaling (U+SH)	360~520			≤156
Bars, semi-finished products, wire; t＜10	Cold Drawing (K)	560~800	≥440	≥6
Bars, semi-finished products, wire; 10≤t<16	Cold Drawing (K)	540~780	≥430	≥7
Bars, semi-finished products, wire; 16≤t<40	Cold Drawing (K)	490~740	≥390	≥8
Bars, semi-finished products, wire; 40≤t<63	Cold Drawing (K)	430~680	≥315	≥9
Bars, semi-finished products, wire; 63≤t＜100	Cold Drawing (K)	390~640	≥265	≥10
Bar, Semi-finished, Wire; t≤100	Cold Drawn and Stress Relief (K+S)	≤550

①A structure is usually defined first, followed by heat treatment (e.g., K+V). When the sequence is reversed, especially for steels such as 45S20, 45SPb20, and 60SPb20, the values to be complied with must be agreed upon.
②The minimum transverse elongation in a tensile test applies to steels 9Mn28, 9SMnPb28, 15S10, 10S20, and 10SPb20 in structural or heat-treated states U+SH and K+S.
③Round bars exceeding 50mm in diameter are generally supplied in a peeled condition rather than cold-drawn.

New and Old Grade Replacement List

Corresponding Standard	Grade
DIN 1651-1988	Grade Germany W-Nr.
DIN EN ISO 683-4-2018	Grade

1 Approximate Comparison Table Free-Cutting Structural Steel

United States		Germany		France	United Kingdom
ASTM/AISI	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
1215	G12150	9SMn36	1.0736	S300	240M07

2 Approximate Comparison Table Free-Cutting Structural Steel

International Organization for Standardization	Germany	France	European Standard
ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade
11SMn37	9SMn36	S300	11SMn37	1.0736

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!