Grade Ck35
Germany W-Nr. 1.1181
Corresponding Standard DIN 17200-1987
Classification Carbon Steel
Density 7.85 g/cm3
Ck35 Chemical Element Composition Content (%)
Component C Si Mn P S
Minimum Value 0.32 - 0.5 - -
Maximum Value 0.39 0.4 0.8 0.035 0.03
Ck35 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Reduction of Area
ψ
% 		Hardness
HBW 		Impact Energy Absorption
KV2
J
Steel; All Sizes Softening Annealing (G) ≤183
Steel; d≤16 Quenching and Tempering (V) 630~780 ≥430 ≥17 ≥40 ISO-V
≥35
Steel; 16<d≤40 Quenching and Tempering (V) 600~750 ≥370 ≥19 ≥45 ≥35
40<d≤100 Quenching and Tempering (V) 650~700 ≥320 ≥20 ≥50 ≥35
Bars; 16<d≤100 Normalizing (N) 490~640 ≥275 ≥21
Flat steel; d≤16 Normalizing (N) 480~670 ≥300 Longitudinal
≥21
Flat steel; 16<d≤100 Normalizing (N) 480~670 ≥275 ≥21
Flat Steel; 100<d≤160 Normalizing (N) 460~650 ≥245 ≥19
New and Old Grade Replacement List
Corresponding Standard Grade
DIN 17200-1987
Grade
Germany W-Nr.
DIN EN ISO 683-1-2018
Grade
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO DIN EN/DIN W-Nr. NF EN/NF GOST SS BS EN/BS
35 U20352 S35C S35C SM35C 1035 G10350 C35E4 C35E
Ck35 		1.1181 C35E
XC38 		35 1572 C35E
080M36
2 Approximate Comparison Table
China Japan United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB JIS ASTM ISO DIN EN/DIN NF EN/NF EN Numerical Grade GOST SS BS EN/BS
35 S35C 1035 C35E4 Ck35 XC38
XC38H1 		C35E 1.1181 35 1572 080M36
CFS6
Ck35 Corresponding Standards(Same grade name, different standards)
1 DIN 17200-1987
Ck35 1.1181
2 DIN 17204-1990
Ck35 1.1181
3 DIN 17240-1976
Ck 35 1.1181
4 DIN 1652-1963
Ck35 1.1181

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!