C60 - ISO 683-18-2014

C60 Chemical Element Composition Content (%)

Component	C	Si ^①	Mn	P	S	Cr	Ni	Cu	Mo	More
Minimum Value	0.57	0.1	0.6	-	-	-	-	-	-	Cr+Mo+Ni≤0.63
Maximum Value	0.65	0.4	0.9	0.045	0.045	0.4	0.4	0.3	0.1	Cr+Mo+Ni≤0.63

C60 Mechanical Properties

	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
5≤t≤10	Cold drawn (+C)	800~1150	≥630	≥5
10＜t≤16	Cold drawn (+C)	780~1130	≥550	≥5
16＜t≤40	Cold drawn (+C)	730~1100	≥480	≥6
16＜t≤100	As-rolled + peeled (+SH)	670~940			196~278

1 Approximate Comparison Table

China	Japan	International Organization for Standardization	European Standard
GB	JIS	ISO	EN	Numerical Grade
60	S58C	C60	C60	1.0601

2 Approximate Comparison Table

China	Japan	United States	International Organization for Standardization	Germany	European Standard		Russia	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	EN	Numerical Grade	GOST	BS EN/BS
60	S58C	1060	C60	C60	C60	1.0601	60 60G	070M60

3 Approximate Comparison Table

China		Japan	United States	International Organization for Standardization	France	Russia	United Kingdom
GB	ISC	JIS	ASTM/AISI	ISO	NF EN/NF	GOST	BS EN/BS
60 (GB/T 699-1999)	U20602	S58C	1060	C60 C60E4 C60M2 (ISO 630-1:1987)	C60 XC60	60	060A62

C60 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!