C35R - ISO 683-18-2014

C35R Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	More
Minimum Value	0.32	0.1	0.5	-	0.02	-	-	-	-	Cr+Mo+Ni≤0.63
Maximum Value	0.39	0.4	0.8	0.025	0.04	0.4	0.4	0.3	0.1	Cr+Mo+Ni≤0.63

C35R Mechanical Properties

	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW	Impact Energy Absorption KV2 J
5≤t≤10	Cold drawn (+C)	650~1000	≥510	≥6
10＜t≤16	Cold drawn (+C)	600~950	≥420	≥7
16＜t≤40	Cold drawn (+C)	580~880	≥320	≥8
40＜t≤63	Cold drawn (+C)	550~840	≥300	≥9
63＜t≤100	Cold drawn (+C)	520~800	≥270	≥9
16＜t≤100	As-rolled + peeled (+SH)	520~700			156~204
16＜t≤40	Quenched and tempered and peeled (+QT+SH)	600~750	≥370	≥19		≥35
40＜t≤100	Quenched and tempered and peeled (+QT+SH)	550~700	≥320	≥20		≥35
5≤t≤10	Quenched and tempered + cold drawn (+QT +C)	750~950	≥525	≥9
10＜t≤16	Quenched and tempered + cold drawn (+QT +C)	700~900	≥490	≥9
16＜t≤40	Quenched and tempered + cold drawn (+QT +C)	650~850	≥455	≥10
40＜t≤63	Quenched and tempered + cold drawn (+QT +C)	570~770	≥400	≥11
63＜t≤100	Quenched and tempered + cold drawn (+QT +C)	550~750	≥385	≥12

Approximate Comparison Table

United States	International Organization for Standardization	Germany	France	European Standard		United Kingdom
ASTM	ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	BS EN/BS
1035	C35R C35M2	C35 Cm35	XC38H1u	C35R	1.1180	080M36

C35R Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!