56SiCr7 1.7106 - DIN EN 10089-2003

Grade	56SiCr7
Germany W-Nr.	1.7106
Corresponding Standard	DIN EN 10089-2003 Hot-rolled steels for quenched and tempered springs Technical delivery conditions
Classification	Spring Steel
Properties	Strength Elasticity Fatigue Resistance Quench Hardness

56SiCr7 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	More
Minimum Value	0.52	1.6	0.7	-	-	0.2	Cu+10Sn ±0.60
Maximum Value	0.6	2	1	0.025	0.025	0.45	Cu+10Sn ±0.60

56SiCr7 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
Bar, rod	Quenching and Tempering (+QT)	1500~1800	≥1350	≥6	≥25		KU ≥8
Bar, rod	Cold Shearing Treatment (+S)					≤280
Bar, rod	Softening Annealing (+A)					≤248
Bar, rod	Spheroidizing Annealing (+AC)					≤230

56SiCr7 Corresponding Standards(Same grade name, different standards)