60CrMo3-1 1.7239 - DIN EN 10089-2003

Grade	60CrMo3-1
Germany W-Nr.	1.7239
Corresponding Standard	DIN EN 10089-2003 Hot-rolled steels for quenched and tempered springs Technical delivery conditions
Classification	Spring Steel
Properties	Strength Elasticity Fatigue Resistance Quench Hardness

60CrMo3-1 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Mo	More
Minimum Value	0.56	-	0.7	-	-	0.7	0.06	Cu+10Sn ±0.60
Maximum Value	0.64	0.4	1	0.025	0.025	1	0.15	Cu+10Sn ±0.60

60CrMo3-1 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
Bar, rod	Quenching and Tempering (+QT)	1450~1750	≥1300	≥6	≥30	-	KU ≥8
Bar, rod	Cold Shearing Treatment (+S)	-	-	-	-	≤280	-
Bar, rod	Softening Annealing (+A)	-	-	-	-	≤248	-
Bar, rod	Spheroidizing Annealing (+AC)	-	-	-	-	≤230	-

60CrMo3-1 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!