HS 2-9-2 1.3348 - DIN EN ISO 4957-2018

Grade	HS 2-9-2
Germany W-Nr.	1.3348
Corresponding Standard	DIN EN ISO 4957-2018 Tool steels
Classification	Alloy Steel
Density	7.85 g/cm³

HS 2-9-2 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Mo	W	V
Minimum Value	0.95	-	-	-	-	3.5	8.2	1.5	1.7
Maximum Value	1.05	0.7	0.4	0.03	0.03	4.5	9.2	2.1	2.2

• Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser, other than for the purpose of finishing the heat . All reasonable precautions shall be taken to prevent the addition from scrap or other material used in the manufacture, of such elements which affect the hardenability, mechanical properties and applicability.

HS 2-9-2 Mechanical Properties

	Hardness HBW
Softening Annealed	≤269
Quenching and Tempering	HRC ≥64

New and Old Grade Replacement List

Corresponding Standard	Grade
DIN 17350-1980	Grade Germany W-Nr.
DIN EN ISO 4957-2018	Grade Germany W-Nr.

1 Approximate Comparison Table High-Speed Tool Steels

Japan	International Organization for Standardization	Germany		European Standard
JIS	ISO	DIN EN/DIN	W-Nr.	EN	Numerical Grade
SKH58	HS2-9-2	HS2-9-2 (S 2-9-2)	1.3348	HS2-9-2	1.3348

2 Approximate Comparison Table High-Speed Steel 1

China	Japan	United States	International Organization for Standardization	Germany		France	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
W2Mo9Cr4V2	SK H58	M7	HS2-9-2	S2-9-2	1.3348	Z100DCWV09-04-02-02	BM7

3 Approximate Comparison Table High-Speed Steel 2

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Sweden

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

SS₁₄

BS EN/BS

W2Mo9Cr4V2

T62942

SKH58

T11307

HS 2-9-2

S 2-9-2

1.3348

HS 2-9-2

2782

HS 2-9-2

HS2-9-2 Corresponding Standards(Same grade name, different standards)

1	DIN EN ISO 4957-2018
	HS 2-9-2 1.3348
2	ISO 4957-2018
	HS 2-9-2 1.3348

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!