102Cr6 1.2067 - DIN EN ISO 4957-2018

Grade	102Cr6
Germany W-Nr.	1.2067
Corresponding Standard	DIN EN ISO 4957-2018 Tool steels
Classification	Alloy Steel
Density	7.85 g/cm³

102Cr6 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr
Minimum Value	0.95	0.15	0.25	-	-	1.35
Maximum Value	1.1	0.35	0.45	0.03	0.03	1.65

• Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser, other than for the purpose of finishing the heat . All reasonable precautions shall be taken to prevent the addition from scrap or other material used in the manufacture, of such elements which affect the hardenability, mechanical properties and applicability.

102Cr6 Mechanical Properties

	Hardness HBW
Soft annealing (+A)	≤223
Quenching and Tempering	HRC ≥60

1 Approximate Comparison Table Alloy cold-work tool steel

International Organization for Standardization	Germany		European Standard
ISO	DIN EN/DIN	W-Nr.	EN	Numerical Grade
102Cr6	102Cr6	1.2067	102Cr6	1.2067

2 Approximate Comparison Table alloy tool stee

China	United States	Germany		France	Russia	United Kingdom
GB	ASTM/AISI	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
9Cr2	L7	100Cr6	1.2067	Y100C6	9Х	BL3

102Cr6 Corresponding Standards(Same grade name, different standards)

1	EN 10132-4-2002
	102Cr6 1.2067
2	DIN EN ISO 4957-2018
	102Cr6 1.2067
3	ISO 4957-2018
	102Cr6 1.2067
4	DIN EN 10132-4-2000(+AC:2002)
	102Cr6 1.2067
5	EN 10132-2021
	102Cr6 1.2067

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!