C2C 1.0314 - EN 10263-2-2017

Grade	C2C
European Standard Steel Grade	1.0314
Corresponding Standard	EN 10263-2-2017 Steel rod,bars and wire for cold heading and cold extrusion - Part 2: Technical delivery conditions for steels not intended for heat treatment after cold working
Classification	Carbon Steel

C2C Chemical Element Composition Content (%)

Component	C	Si	Mn ^①	P	S	Al ^②
Minimum Value	-	-	0.2	-	-	0.02
Maximum Value	0.03	0.1	0.4	0.02	0.025	0.06

C2C Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
Coil, steel bar; 5 < d ≤ 100	Hot Rolled or Untreated and Pickled (+U or +U+PE)	≤360	≥75
Steel bar, wire; 5 < d ≤ 10	Untreated and Cold Drawn (+U+C)	≤450	≥70
Steel bar, wire; 10 < d ≤ 40	Untreated and Cold Drawn (+U+C)	≥440	≥70
Steel Bar, Steel Wire; 40<d≤100	Untreated and Cold Drawn (+U+C)	≤440	≥68
Steel rods, steel wires; 2＜d≤5	Untreated, Cold Drawn, and Spheroidized (+U+C+AC)	≤310	≥80
Steel Bar, Steel Wire; 5<d≤100	Untreated, Cold Drawn, and Spheroidized (+U+C+AC)	≤300	≥80
Coil bars, steel bars; 2＜d≤5	Untreated, Cold Drawn, Spheroidized, and Flattened (+U+C+AC+LC)	≤350	≥75
Coil, steel bar; 5 < d ≤ 100	Untreated, Cold Drawn, Spheroidized, and Flattened (+U+C+AC+LC)	≤340	≥75

Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

Japan	International Organization for Standardization	European Standard
JIS	ISO	EN	Numerical Grade
SWRCH6A	C2C C4C	C2C C4C	1.0314 1.0303

C2C Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!