Grade ZG00Cr18Ni10
China ISC 301
Corresponding Standard GB 2100-1980
Technical conditions for stainless acid-resistant steel castings
Classification Austenitic Stainless Steel
Properties Corrosion Resistance
ZG00Cr18Ni10 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni
Minimum Value - - 0.8 - - 17 8
Maximum Value 0.03 1.5 2 0.04 0.03 20 12
ZG00Cr18Ni10 Mechanical Properties
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Reduction of Area
ψ
%
Quenching at 1050~1100°C, water cooling ≤490 ≤245 ≤25 ≤32
1 Approximate Comparison Table Corrosion-Resistant Cast Steels
China Japan United States Germany France Russia United Kingdom
GB JIS ASTM DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG00Cr18Ni10 SUS19 CF3 G-X2CrNi18 9 1.4306 Z2CN18.10M Х18Н8Л(旧号) 304C12
2 Approximate Comparison Table Heat-Resistant Cast Steels and Alloys
China Japan United States Germany France Russia United Kingdom
GB JIS ASTM UNS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG00Cr18Ni10 SCS19 CF3 J92500 G-X2CrNi18 9 1.4036 Z2CN18.10M 03Х18Н11 304C12