Grade ZG1Cr18Ni9Ti
China ISC 305
Corresponding Standard GB 2100-1980
Technical Conditions for Stainless Acid-Resistant Steel Castings
Classification Austenitic Stainless Steel
Properties Corrosion Resistance
ZG1Cr18Ni9Ti Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni More
Minimum Value - - 0.8 - - 17 8 Ti:5(C-0.02)~0.7
Maximum Value 0.12 1.5 2 0.045 0.03 20 11
ZG1Cr18Ni9Ti Mechanical Properties
Heat Treatment or Condition
Tensile Strength
σb
Mpa
Yield Point
σs
Mpa
Elongation or Extension Rate
δ
%
Reduction of Area
ψ
%
Quenching at 950~1050°C, water cooling ≤441 ≤196 ≤25 ≤32
Approximate Comparison Table Heat-Resistant Cast Steels and Alloys
China United States Russia
GB ASTM UNS GOST
ZG1Cr18Ni9Ti CF8M J92900 12Х18Н9Т

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!