Home Material GB 2100-1980
简体 | 繁體
Grade ZG1Cr13
China ISC 101
Corresponding Standard GB 2100-1980
Technical Conditions for Stainless Acid-Resistant Steel Castings
Classification Cast Steel
ZG1Cr13 Chemical Element Composition Content (%)
Component C Si Mn P S Cr
Minimum Value 0.08 - - - - 12
Maximum Value 0.15 1 0.6 0.04 0.03 14
ZG1Cr13 Mechanical Properties
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Reduction of Area
ψ
%
Annealing 950°C, quenching 1050°C, tempering 750°C, water or air cooling ≤548.8 ≤392 ≤20 ≤50
1 Approximate Comparison Table Corrosion-Resistant Cast Steels
China Japan United States Germany France Russia United Kingdom
GB JIS ASTM DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG1Cr13 SUS1 CA15 G-X8Cr14
X15Cr13 		1.4008
1.4024 		Z12C13M 15Х13Л 410C21
2 Approximate Comparison Table Heat-Resistant Cast Steels and Alloys
China Japan United States Germany France Russia United Kingdom
GB JIS ASTM UNS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG1Cr13 SCS1 CA15 J91150 G-X7Cr13
G-X10Cr13 		1.4001
1.4006 		Z12C13M 15Х13Л 410C21