ZG07Cr19Ni11Mo2 - GB /T 2100-2002

Grade	ZG07Cr19Ni11Mo2
Corresponding Standard	GB /T 2100-2002 Corrosion-Resistant Steel Castings for General Applications
Classification	Cast Steel

ZG07Cr19Ni11Mo2 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo
Minimum Value	-	-	-	-	-	17	9	2
Maximum Value	0.07	1.5	1.5	0.04	0.03	20	12	2.5

ZG07Cr19Ni11Mo2 Mechanical Properties

thickness t mm	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
t≤150	≥440	≥180	≥30	≥60

1 Approximate Comparison Table Cast Steel

China	United States	International Organization for Standardization
GB	UNS	ISO	Numerical Grade
ZG07Cr19Ni11Mo2	J92900	GX5CrNiMo19-11-2	1.4408

2 Approximate Comparison Table Corrosion-Resistant Cast Steels

3 Approximate Comparison Table Corrosion-Resistant Cast Steels

China		Taiwan, China	Japan	South Korea	International Organization for Standardization	Germany		France	Russia	Sweden	United Kingdom
GB	ISC	CNS	JIS	KS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS₁₄	BS EN/BS
ZG07Cr19Ni11Mo2	C53162	SCS 14A	SCS 14X	SSC 14A	GX5CrNiMo19-11-2	GX5CrNiMo19-11-2	1.4408	Z6CND18.12M	0Х18Н10Т2С2М2Л	2343	GX5CrNiMo19

ZG07Cr19Ni11Mo2 Corresponding Standards(Same grade name, different standards)