ZG07Cr19Ni11Mo3 - GB /T 2100-2002

Grade	ZG07Cr19Ni11Mo3
Corresponding Standard	GB /T 2100-2002 Corrosion-Resistant Steel Castings for General Applications
Classification	Cast Steel

ZG07Cr19Ni11Mo3 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo
Minimum Value	-	-	-	-	-	17	9	3
Maximum Value	0.07	1.5	1.5	0.04	0.03	20	12	3.5

ZG07Cr19Ni11Mo3 Mechanical Properties

thickness t mm	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
t≤150	≥440	≥180	≥30	≥60

Approximate Comparison Table Steel castings for pressure purposes

China	Taiwan, China	Japan	South Korea	United States		International Organization for Standardization	Germany		France	Sweden	United Kingdom
GB	CNS	JIS	KS	ASTM	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	SS₁₄	BS EN/BS
ZG07Cr19Ni11Mo3	SCS14A	SCS14A	SCS14A	CF8M	J92900	GX5CrNiMo19-11-2	GX6CrNiMo18-10	1.4408	Z6CN18.12-M	2343-12	≈GX5CrNiMo19-11-2

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!