W2Mo9Cr4VCo8 - GB 9943-1988

Grade	W2Mo9Cr4VCo8
Corresponding Standard	GB 9943-1988 High Speed Tool Steel Bars-Technical Requirement
Classification	Tool Steel

W2Mo9Cr4VCo8 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	W	V	Co
Minimum Value	1.05	0.15	0.15	-	-	3.5	-	-	9	1.15	0.95	7.75
Maximum Value	1.15	0.65	0.4	0.03	0.03	4.25	0.3	0.25	10	1.85	1.35	8.75

W2Mo9Cr4VCo8 Mechanical Properties

1 Approximate Comparison Table High-Speed Tool Steels

China	Japan	South Korea	United States	International Organization for Standardization	Germany	United Kingdom
GB	JIS	KS	ASTM/AISI	ISO	DIN EN/DIN	BS EN/BS
W2Mo9Cr4VCo8	SKH59	SKH59	M42	HS2-9-1-8	S2-10-1-8	BM42

2 Approximate Comparison Table High-Speed Steel 1

China	Japan	United States	International Organization for Standardization	Germany		France	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
W2Mo9Cr4VCo8	YXM34	M33 M34	HS2-9-1-8	S2-9-2-8	1.3249	Z110DKCWV09-08-04-02-01	BM34

3 Approximate Comparison Table High-Speed Steel 2

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Sweden

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

SS₁₄

BS EN/BS

W2Mo9Cr4VCo8

T72948

SKH59

M42

T11342

HS 2-9-1-8

S 2-10-1-8

1.3247

HS 2-9-1-8

2716

HS 2-9-1-8
BM42

4 Approximate Comparison Table High-Speed Steel 3

China		Japan	United States		International Organization for Standardization	European Standard	Russia
GB	ISC	JIS	ASTM	UNS	ISO	EN	GOST
W2Mo9Cr4VCo8	T72948	SKH59	M42	T11342	HS 2-9-1-8	HS 2-9-1-8	Р2АМ9К5

W2Mo9Cr4VCo8 Corresponding Standards(Same grade name, different standards)