SKH 3 - JIS G 4403-2005

SKH 3 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Cu	W	V	Co
Minimum Value	0.73	-	-	-	-	3.8	-	17	0.8	4.5
Maximum Value	0.83	0.45	0.4	0.03	0.03	4.5	0.25	19	1.2	5.5

SKH 3 Mechanical Properties

condition	Heat Treatment or Condition	Hardness HBW
Bar, forging	Annealing	≤269
Bar, forging	Quenching + Tempering	HRC ≥64

1 Approximate Comparison Table High-speed tool steels

China	Japan	South Korea	United States	International Organization for Standardization	Germany	United Kingdom
GB	JIS	KS	ASTM/AISI	ISO	DIN EN/DIN	BS EN/BS
W18Cr4VCo5	SKH3	SKH3	T4	HS18-1-1-5	S18-1-2-5	T4

2 Approximate Comparison Table

China

Taiwan, China

Japan

South Korea

United States

Germany

France

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM

UNS

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

SS₁₄

BS EN/BS

W18Cr4VCo5

T71845

SKH 3

T12004

S 18-1-2-5

1.3255

HS 18-1-2-5

≈Р18К5Ф2

254

HS 18-1-2-5
BT4