65 U20652 - GB /T 1222-2016

65 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu ^*
Minimum Value	0.62	0.17	0.5	-	-	-	-	-
Maximum Value	0.7	0.37	0.8	0.03	0.03	0.25	0.35	0.25

65 Mechanical Properties

	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
Quenching and Tempering	≥980	≥785	≥9	≥35	-
Hot Rolled (WHR)	-	-	-	--	≤285

1 Approximate Comparison Table High-Quality Carbon Structural Steel

China		United States		International Organization for Standardization	Germany		France	Russia	Sweden	United Kingdom
GB	ISC	ASTM/AISI	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS	BS EN/BS
65	U20652	1065	G10650	SL SM	Ck67	1.1231	XC65	65	1770	060A67

2 Approximate Comparison Table Spring Steel

China		Japan	United States		International Organization for Standardization	Germany		France	Russia	Sweden	United Kingdom
GB	ISC	JIS	AISI	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS₁₄	BS EN/BS
65	U20652	SUP2	1065	G10650	Type DC	Ck67	1.1231	XC65	65	1770	060A67

3 Approximate Comparison Table High-Quality Carbon Structural Steel

4 Approximate Comparison Table Spring Steel

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM/AISI	ISO	EN	Numerical Grade
65 (GB/T 1222-2016)	U20652	S65-CSP (JIS G4802:2005)	1065 (ASTM A29/A29M:2005)	C60E4 (ISO 683-18:1996)	C60E (EN 10083-1:1991+A1:1996)	1.1221

5 Approximate Comparison Table Spring Steel 1

65 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!