55CrMn A22553 - GB /T 1222-2016

55CrMn Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu ^*
Minimum Value	0.52	0.17	0.65	-	-	0.65	-	-
Maximum Value	0.6	0.37	0.95	0.025	0.02	0.95	0.35	0.25

55CrMn Mechanical Properties

	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
Quenching and Tempering	≥1225	≥1080	≥9	≥20	-
Hot Rolled (WHR)	-	-	-	-	≤321

Approximate Comparison Table Spring Steel

China		Taiwan, China	Japan	South Korea	United States		International Organization for Standardization	Germany		France	United Kingdom
GB	ISC	CNS	JIS	KS	AISI	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
55CrMnA	A22553	SUP9	SUP9	SPS5	5155	G51550	55Cr3	55Cr3	1.7176	55C3	≈527A60