1035 - GB /T 3191-2019

Grade	1035
Corresponding Standard	GB /T 3191-2019 Extrusion rods and bars of aluminium and aluminium alloys
Classification	Aluminum and Aluminum Alloys

1035 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %
Bar; d≤150	1035O	O	60~120	≥25
Bar; d≤150	1035H112	H112	≥60	≥25

① O = annealed ;
② H = work hardened;
③ T6 = solution heat treated + artificial aged;
④ T1 = high temperature molding + natural aged;
⑤ T3 = after solution heat treated, cold processing, and then natural aged to a basically stable;
⑥ T4 = after solution heat treated, natural aged to a basically stable;
⑦ T5 = cooled by high temperature molding, and then artificially aged to a basically stable;
⑧ T7 = after solution heat treated, overaged;
⑨ T8 = after solution heat treated, cold processing , and then artificial aged
◎ d = round rod diameter or thickness of square rod or hexagonal rod, t = square rod or hexagonal rod thickness, unit mm

Approximate Comparison Table Wrought aluminum and aluminum alloy

China	Japan	United States		International Organization for Standardization		European Standard
GB	JIS	ASTM	UNS	ISO	Numerical Grade	EN
1035	1035 A91035	1035	A91035	Al99.35	A91035	EN-AW-Al99.35

1035 Corresponding Standards(Same grade name, different standards)

1	SAE
	1035 1035
2	ASTM A29/A29M-2012
	1035 G10350 (C1035)
3	GB /T 3190-2008
	1035
4	ASTM A29/A29M-2005
	1035 G10350 (C1035)
5	GB /T 3195-2016
	1035
6	ASTM A1040-2010
	1035 G10350 (C1035)
7	ASTM A510/A510M-2013
	1035 G10350 1035
8	SAE J403-2014
	1035 G10350
9	ASTM A29/A29M-2020
	1035 G10350 (C1035)
10	GB /T 3190-2020
	1035
11	GB /T 3191-2019
	1035

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!