5A03 LF3 - GB /T 3191-2019

Grade	5A03
Other Names
Corresponding Standard	GB /T 3191-2019 Extrusion Rods and Bars of Aluminium and Aluminium Alloys
Classification	Aluminum and Aluminum Alloys

5A03 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Bar; d≤150	5A03O	O	≥175	≥80	≥13
Bar; d≤150	5A03H112	H112	≥175	≥80	≥13

① O = annealed ;
② H = work hardened;
③ T6 = solution heat treated + artificial aged;
④ T1 = high temperature molding + natural aged;
⑤ T3 = after solution heat treated, cold processing, and then natural aged to a basically stable;
⑥ T4 = after solution heat treated, natural aged to a basically stable;
⑦ T5 = cooled by high temperature molding, and then artificially aged to a basically stable;
⑧ T7 = after solution heat treated, overaged;
⑨ T8 = after solution heat treated, cold processing , and then artificial aged
◎ d = round rod diameter or thickness of square rod or hexagonal rod, t = square rod or hexagonal rod thickness, unit mm

Approximate Comparison Table Wrought Aluminum and Aluminum Alloy

China		United States		International Organization for Standardization		France	European Standard	Australia
GB	ISC	ASTM	UNS	ISO	Numerical Grade	NF EN/NF	EN	Australian Standard AS
5A03 (LF3)	5042	5042	A95042	AlMg3.5Mn	A95042	A-G3.5M 5042 A95042	EN AW-AlMg3.5Mn	5042 A95042

5A03 Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	5A03 (LF3)
2	GB /T 3190-2020
	5A03 (LF3)
3	GB /T 3191-2019
	5A03 LF3
4	GJB 2054-1994
	5A03 LF3 三号防锈铝
5	GJB 2379-1995
	5A03 LF3 三号防锈铝
6	GB /T 3880.1-2012
	5A03 (LF3)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!