6061 LD30 - GB /T 3191-2019

Grade	6061
Old Grade
Corresponding Standard	GB /T 3191-2019 Extrusion rods and bars of aluminium and aluminium alloys
Classification	Aluminum and Aluminum Alloys

6061 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Bar; d≤150	6061T6	T6、T6510、T6511	≥260	≥240	≥8	95
Bar; d≤150	6061T6510	T6、T6510、T6511	≥260	≥240	≥8	95
Bar; d≤150	6061T6511	T6、T6510、T6511	≥260	≥240	≥8	95
Bar; d≤150	6061T4	T4、T4510、T4511	≥180	≥110	≥15	65
Bar; d≤150	6061T4510	T4、T4510、T4511	≥180	≥110	≥15	65
Bar; d≤150	6061T4511	T4、T4510、T4511	≥180	≥110	≥15	65

① O = annealed ;
② H = work hardened;
③ T6 = solution heat treated + artificial aged;
④ T1 = high temperature molding + natural aged;
⑤ T3 = after solution heat treated, cold processing, and then natural aged to a basically stable;
⑥ T4 = after solution heat treated, natural aged to a basically stable;
⑦ T5 = cooled by high temperature molding, and then artificially aged to a basically stable;
⑧ T7 = after solution heat treated, overaged;
⑨ T8 = after solution heat treated, cold processing , and then artificial aged
◎ d = round rod diameter or thickness of square rod or hexagonal rod, t = square rod or hexagonal rod thickness, unit mm

6061 Corresponding Standards(Same grade name, different standards)

1	GB /T 3190-2008
	6061 (LD30)
2	JIS H 4040-2006
	6061 A6061 W A6061 BD A6061 BE
3	GB /T 3195-2016
	6061 (LD30)
4	DIN 1725-1-1983
	6061 AlMg1SiCu 3.3211
5	GB /T 3190-2020
	6061 (LD30)
6	JIS H 4040-2015
	6061 A6061 BD A6061 BE A6061 W
7	GB /T 3191-2019
	6061 (LD30)
8	GJB 1741A-2008
	6061 (LD30)
9	GB /T 29729-2022
	6061 (LD30)
10	GB /T 3880.1-2012
	6061 (LD30)