Grade	JFE-HITEN980LE
Brand/Supplier	Japan -> JFE Steel
Classification	Alloy Steel
Properties	Strength Weldability

JFE-HITEN980LE Chemical Element Composition Content (%)

	Component	C	Si	Mn	P	S	Cr	Mo	V	Nb	B
板厚t≤32	Minimum Value	-	-	-	-	-	-	-	-	-	-
板厚t≤32	Maximum Value	0.18	0.4	1.4	0.02	0.015	0.8	0.6	0.1	0.03	0.005

	Component	C	Si	Mn	P	S	Cr	Mo	V	Nb	B
板厚32<t≤50.8	Minimum Value	-	-	-	-	-	-	-	-	-	-
板厚32<t≤50.8	Maximum Value	0.18	0.4	1.4	0.02	0.015	1.5	0.8	0.1	0.03	0.005

	Component	C	Si	Mn	P	S	Cr	Mo	V	Nb	B
板厚50.8<t≤101.6	Minimum Value	-	-	-	-	-	-	-	-	-	-
板厚50.8<t≤101.6	Maximum Value	0.18	0.4	1.4	0.02	0.015	1.5	0.8	0.1	0.03	0.005

JFE-HITEN980LE Mechanical Properties

thickness t mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
5＜t≤6	Quenching and Tempering	980~1150	≥900	≥12	-
6＜t≤16	Quenching and Tempering	980~1150	≥900	≥12	-40°C ≥40
16＜t≤50.8	Quenching and Tempering	980~1150	≥900	≥19	-40°C ≥40
50.8＜t≤101.6	Quenching and Tempering	880~1080	≥830	-	-40°C ≥40

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!