S10C - JIS G 4051-2016

Grade	S10C
Corresponding Standard	JIS G 4051-2016 Carbon Steels for Machine Structural Use
Brand/Supplier	-> POSCO Japan -> NSSC -> BAOSTEEL
Classification	Carbon Steel

S10C Chemical Element Composition Content (%)

	Component	C	Si	Mn	P	S	Cr	Ni	Cu	More
本标准	Minimum Value	0.08	0.15	0.3	-	-	-	-	-	Ni+Cr≤0.35
本标准	Maximum Value	0.13	0.35	0.6	0.03	0.035	0.2	0.2	0.3	Ni+Cr≤0.35

	Component	C	Si	Mn	P	S	More
宝钢(热轧钢板)	Minimum Value	0.08	0.15	0.3	-	-
宝钢(热轧钢板)	Maximum Value	0.13	0.35	0.6	0.015	0.025

1 Approximate Comparison Table High-Quality Carbon Structural Steel

China

Taiwan, China

Japan

South Korea

United States

Germany

France

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

U20102

S10C

SM10C

1010

G10100

C10
Ck10

1.0301
1.1121

C10
XC10

1265

040A10
045M10

2 Approximate Comparison Table Non-Alloy Surface Hardening Steel

Japan	International Organization for Standardization	European Standard
JIS	ISO	EN	Numerical Grade
S10C	C10E	C10E	1.1121

3 Approximate Comparison Table High-Quality Carbon Structural Steel

China	Japan	United States	International Organization for Standardization	European Standard
GB	JIS	ASTM/AISI	ISO	EN
GB/T 699-2015 08	JIS G4051:2005 JIS G3506:2004 S10C	ASTM A29/A29M:2005 1008	ISO 683-18:1996 C10	EN 10083-1:1991+A1:1996 EN 10084:1998 C10E

4 Approximate Comparison Table High-Quality Carbon Structural Steel

5 Approximate Comparison Table High-Quality Carbon Structural Steel

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM/AISI	ISO	EN	Numerical Grade
10 (GB/T 699-2015)	U20102	S10C (JIS G4051:2005) (JIS G3506:2004)	1010 (ASTM A29/A29M:2005)	C10 (ISO 683:1986)	C10E (EN 10083-1:1991+A1:1996) (EN 10084:1998)	1.1121

S10C Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!