G-X6CrNi 18 9 1.4308 - DIN 17445-1984

Grade	G-X6CrNi 18 9
Germany W-Nr.	1.4308
Corresponding Standard	DIN 17445-1984 Stainless Steel Castings -technical Delivery Conditions
Classification	Cast Steel
Properties	Corrosion Resistance
Density	7.9 g/cm³

G-X6CrNi 18 9 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni
Minimum Value	-	-	-	-	-	18	9
Maximum Value	0.07	2	1.5	0.045	0.03	20	11

G-X6CrNi 18 9 Mechanical Properties

condition	Test Temperature	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW	Impact Energy Absorption KV2 J
Casting	Room Temperature	Quenching	440~640	≥175	≥20	130~200	≥60
Casting		Quenching		≥145
				≥125
				≥115
				≥105
				≥100

1 Approximate Comparison Table Corrosion-Resistant Cast Steels

China

Taiwan, China

Japan

South Korea

United States

Germany

France

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM

UNS

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

SS₁₄

BS EN/BS

ZG07Cr19Ni9

C53048

SCS 13A

SSC 13A

CF8

J92600

GX5CrNi19-10

1.4308

Z2CN18.10M

07Х18Н9Л

2333

304C15

2 Approximate Comparison Table Corrosion-Resistant Cast Steels

China		Taiwan, China	Japan	South Korea	International Organization for Standardization	Germany		France	Russia	Sweden	United Kingdom
GB	ISC	CNS	JIS	KS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS₁₄	BS EN/BS
ZG07Cr19Ni9	C53048	SCS 13	SCS 13X	SSC 13	GX5CrNi19-9	GX5CrNi19-10	1.4308	Z2CN18.10M	07Х18Н9Л	2333	304C15

3 Approximate Comparison Table Corrosion-Resistant Cast Steels

4 Approximate Comparison Table Heat-Resistant Cast Steels and Alloys