ZAlCu5MnCdVA ZL205A - GB /T 1173-2013

Grade	ZAlCu5MnCdVA
China ISC	ZL205A
Corresponding Standard	GB /T 1173-2013 Casting aluminum alloy
Classification	Aluminum and Aluminum Alloys
Density	2.82 g/cm³

ZAlCu5MnCdVA Chemical Element Composition Content (%)

	Component	Fe	Si	Mn	Cu	Ti	V	Zr	B	Mg	Cd	Other Total	More
S-砂型铸造	Minimum Value	-	-	0.3	4.6	0.15	0.05	0.15	0.005	-	0.15	-	Al:余量
S-砂型铸造	Maximum Value	0.15	0.06	0.5	5.3	0.35	0.3	0.25	0.6	0.05	0.25	0.3	Al:余量

	Component	Fe	Si	Mn	Cu	Ti	V	Zr	B	Mg	Cd	Other Total	More
J-金属型铸造	Minimum Value	-	-	0.3	4.6	0.15	0.05	0.15	0.005	-	0.15	-	Al:余量
J-金属型铸造	Maximum Value	0.16	0.06	0.5	5.3	0.35	0.3	0.25	0.6	0.05	0.25	0.3	Al:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

ZAlCu5MnCdVA Mechanical Properties

casting process	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %	Hardness HBW
S	ZL205A-T5	T5 - Solution Heat Treatment + Incomplete Artificial Aging	≥440	≥7	≥100
S	ZL205A-T6	T6 - Solution Treatment + Full Artificial Aging	≥470	≥3	≥120
S	ZL205A-T7	T7 - Solution Treatment + Stabilization Treatment	≥460	≥2	≥110

ZAlCu5MnCdVA Corresponding Standards(Same grade name, different standards)

1	GB /T 1173-2013
	ZAlCu5MnCdVA ZL205A
2	HB 962-2001
	ZAlCu5MnCdVA ZL205A

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!