ML04Al U40048 - GB /T 28906-2012

Grade	ML04Al
China ISC	U40048
Corresponding Standard	GB /T 28906-2012 Hot Rolled Wire Rod for Cold Heading
Classification	Carbon Steel
Properties	Forgability

ML04Al Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr ^*	Ni ^*	Cu ^*	Al ^**
Minimum Value	-	-	0.2	-	-	-	-	-	0.02
Maximum Value	0.06	0.1	0.4	0.03	0.03	0.2	0.2	0.2	-

ML04Al Mechanical Properties

Tensile Strength σ_b Mpa	Reduction of Area ψ %
≤440	≥60

Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		United States	International Organization for Standardization	European Standard
GB	ISC	ASTM	ISO	EN	Numerical Grade
ML04Al	U40048	1005	CC4A C4C	C4C	1.0303

ML04Al Corresponding Standards(Same grade name, different standards)